Direct comparison between hot pressing and electric field-assisted sintering of submicron alumina

Direct comparison between hot pressing and electric field-assisted sintering of submicron alumina,10.1016/j.actamat.2009.07.043,Acta Materialia,Jochen

Direct comparison between hot pressing and electric field-assisted sintering of submicron alumina   (Citations: 3)
BibTex | RIS | RefWorks Download
This study compares hot pressing (HP) and the electric field-assisted sintering technique (FAST) of two different electrically insulating Al2O3 submicron powders with median particle sizes of 150 and 500nm. Sample geometry, heating schedule, applied pressure and atmosphere were identical for both sintering methods. The densification behavior and characterization of the microstructure revealed that FAST sintered samples reached a higher density compared with HP, in particular for the finer powder. It was found that an increase in dwell time was required to reach the same final density by HP. However, analysis of the sintering curves showed that the densification mechanism for both sintering methods was grain boundary diffusion. Increasing the heating rate up to 150Kmin−1 did not modify the densification mechanism. The sintering trajectory showed that the grain size was only dependent on density and was insensitive to the sintering method, in addition to showing a lack of preferential grain orientation.
Journal: Acta Materialia - ACTA MATER , vol. 57, no. 18, pp. 5454-5465, 2009