Direct synthesis of well-ordered mesoporous Al-SBA-15 and its correlation with the catalytic activity

Direct synthesis of well-ordered mesoporous Al-SBA-15 and its correlation with the catalytic activity,10.1016/j.apcata.2011.04.031,Applied Catalysis A

Direct synthesis of well-ordered mesoporous Al-SBA-15 and its correlation with the catalytic activity  
BibTex | RIS | RefWorks Download
The synthesis of Al-SBA-15 under milder acidic conditions were made through an adjusting the molar H2O/HCl ratio which indicate the formation of Si–O–Al linkages that lead to isomorphous substitution of Si4+ by some Al3+ ions. By adjusting the H2O/HCl molar ratio, Al gets incorporated into the lattice of SBA-15, which is evidenced by XRD, N2 adsorption, TEM, 29Si and 27Al MAS NMR spectroscopic data. Aluminium incorporated SBA-15 samples retained both structural and textural properties of SBA-15. The 27Al MAS NMR confirms that a large proportion of the Al is inserted into tetrahedral positions within the framework. The Al3+ ions could assume a tetrahedral coordination and be part of the hexagonal structure of silica in Al-SBA-15. In the present study, we have examined the effectiveness of Al-SBA-15, as an acid catalyst for the esterification of acetic acid and in benzylation of anisole. The high activity of Al-20 sample in esterification reaction has been attributed to isolated, generally tetrahedrally coordinated, framework Al species. While in benzylation of anisole, the best result was achieved with Al-5 catalyst. The selectivity for benzylanisole increases and that for dibenzylether decreases with increase in the Si/Al ratio of Al-SBA-15.
Journal: Applied Catalysis A-general - APPL CATAL A-GEN , vol. 400, no. 1, pp. 176-184, 2011