Fabrication of a Short-Period Nb3Sn Superconducting Undulator

Fabrication of a Short-Period Nb3Sn Superconducting Undulator,10.1109/TASC.2007.897747,IEEE Transactions on Applied Superconductivity,Daniel R. Dietde

Fabrication of a Short-Period Nb3Sn Superconducting Undulator   (Citations: 3)
BibTex | RIS | RefWorks Download
Lawrence Berkeley National Laboratory develops high-field Nb3Sn magnets for HEP applications. In the past few years, this experience has been extended to the design and fabrication of undulator magnets. Some undulator applications require devices that can operate in the presence of a heat load from a beam. The use of Nb3Sn permits operation of a device at both a marginally higher temperature (5-8 K) and a higher Jc, compared to NbTi devices, without requiring a larger magnetic gap. A half-undulator device consisting of 6 periods (12 coil packs) of 14.5 mm period was designed, wound, reacted, potted and tested. It reached the short sample current limit of 717 A in 4 quenches. The non-Cu Jc of the strand was over 7,600 A /mm2 and the Cu current density at quench was over 8,000 A/mm2 . Magnetic field models show that if a complete device was fabricated with the same parameters one could obtain beam fields of 1.1 T and 1.6 T for pole gaps of 8 mm and 6 mm, respectively.
Cumulative Annual
View Publication
The following links allow you to view full publications. These links are maintained by other sources not affiliated with Microsoft Academic Search.
Sort by: